A History of Valves

A History Made in Metal

vmfall12 history3Pouring bronze in a valve foundryToday’s valve material choices are like a Chinese buffet: Everything imaginable is on the menu. The multitude of choices has grown in response to the demands of customers and their expanding process requirements.


The first Roman valves were made from a bronze alloy very similar to today’s ASTM B62 bronze chemistry. These valves were used in plumbing systems in houses and public buildings. The bronze valves and other engineering discoveries of the Roman period would disappear under the thick cloak of the dark ages, and it wasn’t until the steam era that valve materials became a topic of interest again.


vmfall12 history2A bronze valve for locomotives is shown on the front page of American Machinist in 1885.The 19th century was the era of bronze and iron valves and piping. Looking through that century’s valve catalogs shows that valve material choices were just those two: bronze or iron. As the century neared an end, advances in irons were made including higher-strength cast irons, called ferro-steels, which were developed to meet the rising power plant temperature and pressure requirements.

The first decade of the 20th century saw the introduction of cast steel as a valve material. Improvements in steel-making processes brought steel casting capabilities to the plant floor of the major valve manufacturers. Although steel valves were available during the early part of the century, iron and bronze still were the most popular valve materials.


The materials for valve trim or “trimmings” as it was called a century ago were limited as well. Valve stems, seats and discs were made of bronze, brass or iron. The first improvement in trim materials was the introduction of ­copper-nickel alloys, essentially Monel. This “Monel metal,” as it was called, was very useful because it was harder than anything yet available and also highly corrosion resistant.

The next valve-trim material to gain popularity was Martensitic, 400 series stainless steel. These alloys were highly durable because of their ability to be heat-treated into an extremely hard condition. The 400 series stainless steels, by virtue of the 11-13% chrome content, also were corrosion resistant, and they would be the trim material of choice for 30-40 years until supplanted by cobalt-based “Stellite” materials after World War II.

As the temperatures and pressures increased in the power industry in the 1920s and 1930s, a need arose for higher performance cast steel. The carbon-moly steel alloy was a stopgap that raised the continuous operating temperature of steel valves to 850° F(454° C). Although the carbon-moly steel was useful at higher temperatures, it suffered from creep problems. The pre-WWII period also saw the introduction of the first austenitic stainless-steel alloys (304ss and 316ss), which were vastly superior to the 400 series in corrosion resistance.

Additional alloy steels made their debut as valve materials during the decade following WWII. The chrome/moly steels helped to raise the operating temperatures of cast steel valves above the 1000° F (538° C) range; 1-1/4 Cr. (WC6), 2-1/4 Cr. (WC9), 5 Cr. (C5) and 9 Cr. (C12) were all developed during this period. The first ASTM standard to address these materials was ASTM A157, Alloy Steel Castings for Valves, Flanges and Fittings for High Temperature Service, which was issued in 1950. This standard would later be superseded by ASTM A217. All these alloys also are produced as forgings, with most listed in the ASTM A182 material standard.

vmfall12 history1Making patterns for iron valves During the 1950-1960 time period, new processes in the chemical industry were outstripping the ability of stainless steels to cope with corrosion issues. As a result, higher grades of stainless steels were developed and tried. Alloy 20, stabilized stainless steels (347 & 321) and low-carbon grades (316L and 304L) became popular. However, the ability of these metals to perform satisfactorily would soon be surpassed by the needs of industry yet again. New “super alloys” were developed to meet those needs, including the Hastelloys, Inconels and duplex stainless steels. These materials were very strong at high temperatures and also had impressive corrosion resistance.

Twenty-first century valve manufacturers are still using the popular metals of the past 150 years, but newer materials are always under development. The latest alloy steel to attain great popularity is the “super 9 chrome” C12A cast steel and F91 forged steel, which allow for valve working temperatures of 1200° F (649° C), while providing better creep resistance than C12 material.


Valves that have shafts or stems that move in and out of the pressure envelope require a packing to keep the pressure contained inside the valve. These packings must be flexible, reasonably resilient and able to withstand the highest temperature the valve will see in service. Early packing materials were rope derivatives such as jute and flax. But as operating temperatures rose, these materials proved inadequate. The answer was found in a unique mineral called Chrysotile, which gave us asbestos.

The long fibers of asbestos combined with its temperature resistance made it an outstanding packing and gasket material. Asbestos packing was installed in virtually all commodity steel valves from the 1920s through the 1980s. The material was superior for forming and filling the packing or stuffing box area, and it provided an excellent seal. Unfortunately, some of the same characteristics that made asbestos good packing, such as its fiber shape and size, also made it an unwelcome resident in the human lung. Since virtually every valve manufacturer used asbestos packings or gaskets, all of them have been drawn into lawsuits involving asbestos litigation and mesothelioma.

The replacement of asbestos packing and gaskets took some time, as immediate replacement materials did not work well. Finally, the industry perfected carbon/graphite-based products that have now been the norm for nearly 25 years when high-temperature packing and gasket materials are required.

For low-temperature applications, Teflon is an excellent corrosion-resistant sealing material. Teflon packing and gaskets are standard in today’s nickel alloy and stainless-steel valves. Teflon is also used for other valve components such as ball valve seats. The history of Teflon and ball valve seats is itself an intriguing tale but that tale is for another article.

GREG JOHNSON is president of United Valve (www.unitedvalve.com), Houston, and is a contributing editor to Valve Magazine. He serves as chairman of VMA’s Education & Training Committee, is a member of the VMA Communications Committee and is president of the Manufacturers Standardization Society. Reach him at This email address is being protected from spambots. You need JavaScript enabled to view it..